Biodegradace polyethylenu s prooxidanty

DSpace Repository

Language: English čeština 

Biodegradace polyethylenu s prooxidanty

Show simple item record

dc.contributor.advisor Koutný, Marek
dc.contributor.author Gerych, Pavel
dc.date.accessioned 2010-07-17T03:17:21Z
dc.date.available 2010-07-17T03:17:21Z
dc.date.issued 2008-05-14
dc.identifier Elektronický archiv Knihovny UTB cs
dc.identifier.uri http://hdl.handle.net/10563/7452
dc.description.abstract Cílem diplomové práce bylo sledovat průběh abiotické oxidace a biodegradace polyethylenu s prooxidanty v prostředí půdy a vyzrálého kompostu. Biodegradace byla sledována stanovením plynných produktů procesu metodou plynové chromatografie. V rámci diplomové práce byly testovány tři typy LDPE fólií s prooxidanty. První sadu vzorků tvořily LDPE-1 fólie s prooxidanty na bázi manganu a s obsahem 15 % vápence jako plniva. Vzorky byly nejprve podrobeny urychlenému stárnutí pomocí termooxidace při 70°C po dobu 40 a 80 dní. Po 432 denní biodegradaci v půdním prostředí bylo dosaženo 11,11 % mineralizace u vzorku LDPE-1(40) a 13,98 % u LDPE-1(80). V případě kompostovacích podmínek bylo za 432 dní dosaženo 18,23 % mineralizace u LDPE-1(40) a 18,31 % u LDPE-1(80). Vzorky byly po biodegradaci podrobeny optické a elektronové mikroskopii. Mikroskopické techniky prokázaly přítomnost mikroorganismů na povrchu zkoumaných materiálů. Druhou sadu vzorků tvořily LDPE-2, LDPE-3 fólie o neznámém složení prooxidantů. Vzorky byly nejprve podrobeny urychlenému stárnutí pomocí termooxidace při 70°C po dobu 40 dní. Po 183 denní biodegradaci v půdním prostředí bylo dosaženo 4,34 % mineralizace u vzorku LDPE-2(40) a 5,14 % u LDPE-3(40). V případě kompostovacích podmínek bylo za 92 dní dosaženo 12,28 % mineralizace u LDPE-2(40) a 10,39 % u LDPE-3(40). cs
dc.format 101 s. cs
dc.format.extent 2616542 bytes cs
dc.format.mimetype application/pdf cs
dc.language.iso cs
dc.publisher Univerzita Tomáše Bati ve Zlíně
dc.rights Bez omezení
dc.subject polyethylen cs
dc.subject prooxidanty cs
dc.subject abiotická oxidace cs
dc.subject biodegradace cs
dc.subject polyethylene en
dc.subject prooxidants en
dc.subject abiotic oxidation en
dc.subject biodegradation en
dc.title Biodegradace polyethylenu s prooxidanty cs
dc.title.alternative Biodegradation of polyethylene with prooxidants en
dc.type diplomová práce cs
dc.contributor.referee Růžička, Jan
dc.date.accepted 2008-06-17
dc.description.abstract-translated The main goal of the diploma thesis was to monitor processes of abiotic oxidation and biodegradation of polyethylene containing prooxidants in soil and mature compost environments. Biodegradation was followed by gas chromatography determination of gaseous products. Three types of LDPE films containing prooxidants were investigated. The first set of samples consisted of LDPE-1 films with manganese based prooxidants and with 15 % of calcite as filler. The samples were first subjected to accelerated aging by thermooxidation for 40 and 80 days at 70°C. After 432 days of biodegradation the values of mineralization were about 11,11 % for sample LDPE-1(40) and about 13,98 % for LDPE-1(80) in the soil test and about 18,23 % for sample LDPE-1(40) and 12,31 % for LDPE-1(80) in the compost test. The samples were monitored by optical and electron microscopy after biodegradation. The employed techniques proved the presence of microorganisms on the surface of the materials. The second set of samples included LDPE-2, LDPE-3 films containing prooxidants with unknown composition. The samples were first subjected to accelerated aging by thermooxidation for 40 days at 70°C. After 183 days of biodegradation the values of mineralization were about 4,34 % for LDPE-2(40) and about 5,14 % for LDPE-3(40) in the soil test. After 92 days of biodegradation the values of mineralization were about 12,28 % for LDPE-2(40) and about 10,39 % for LDPE-3(40) in the compost test. en
dc.description.department Ústav inženýrství ochrany živ. prostředí cs
dc.description.result obhájeno cs
dc.parent.uri http://hdl.handle.net/10563/200 cs
dc.parent.uri http://hdl.handle.net/10563/220 cs
dc.thesis.degree-discipline Inženýrství ochrany životního prostředí cs
dc.thesis.degree-discipline Enviromental Protection Engineering en
dc.thesis.degree-grantor Univerzita Tomáše Bati ve Zlíně. Fakulta technologická cs
dc.thesis.degree-grantor Tomas Bata University in Zlín. Faculty of Technology en
dc.thesis.degree-name Ing. cs
dc.thesis.degree-program Chemie a technologie materiálů cs
dc.thesis.degree-program Chemistry and Materials Technology en
dc.identifier.stag 8557
dc.date.assigned 2008-02-19
utb.result.grade A


Files in this item

Files Size Format View
gerych_2008_dp.pdf 2.495Mb PDF View/Open
gerych_2008_vp.doc 33.5Kb Microsoft Word View/Open
gerych_2008_op.doc 40.5Kb Microsoft Word View/Open

This item appears in the following Collection(s)

Show simple item record

Find fulltext

Search DSpace


Browse

My Account